برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 25 g/10 min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmissivity | 2540 µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540 µm | ASTM D1003 | 1.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.1 mm | UL 94 | V-2 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服 | ASTM D638 | 62.0 Mpa |
| tensile strength | 断裂 | ASTM D638 | 65.0 Mpa |
| elongation | 断裂 | ASTM D638 | 120 % |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2300 Mpa |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 93.0 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 54.0 J |
| Impact strength of cantilever beam gap | | ASTM D1822 | 378 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
| High arc combustion index (HAI) | | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | | UL 746 | PLC 2 |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 3.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Suggested injection volume | | | 40 to 60 % |
| Temperature at the rear of the barrel | | | 250 to 270 °C |
| Temperature in the middle of the barrel | | | 260 to 280 °C |
| Temperature at the front of the material cylinder | | | 270 to 295 °C |
| Spray nozzle temperature | | | 265 to 290 °C |
| Processing (melt) temperature | | | 270 to 295 °C |
| Temperature | | | 70 to 95 °C |
| Back pressure | | | 0.300 to 0.700 Mpa |
| screw speed | | | 40 to 70 rpm |
| Exhaust hole depth | | | 0.025 to 0.076 mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 126 °C |
| RTI Elec | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI | | UL 746 | 130 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.