| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 0.947 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.28 g/10min |
| 190°C/21.6kg | ASTM D1238 | 20 g/10min |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| DartImpact | 25.4µm19 | ASTM D1709 | 100 g |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Secant modulus | 1%正割,TD:25µm | ASTM D882A | 1000 MPa |
| tensile strength | MD:屈服,25µm2 | ASTM D882A | 24.1 MPa |
| MD:屈服,25µm3 | ASTM D882A | 23.4 MPa | |
| TD:屈服,25µm4 | ASTM D882A | 25.5 MPa | |
| TD:屈服,25µm5 | ASTM D882A | 26.2 MPa | |
| elongation | MD:断裂,25µm10 | ASTM D882A | 600 % |
| MD:断裂,25µm11 | ASTM D882A | 450 % | |
| TD:断裂,25µm12 | ASTM D882A | 700 % | |
| TD:断裂,25µm13 | ASTM D882A | 600 % | |
| Elmendorf tear strength | MD:25µm14 | ASTM D1922 | 28 g |
| MD:25µm15 | ASTM D1922 | 10 g | |
| TD:25µm16 | ASTM D1922 | 530 g | |
| TD:25µm17 | ASTM D1922 | 1500 g | |
| Water Vapor Transmission Rate | 38°C,25µm | ASTME96 | 7.8 g/m²/24hr |
| film thickness | 25 µm | ||
| Secant modulus | 1%正割,MD:25µm | ASTM D882A | 710 MPa |
| tensile strength | MD:断裂,25µm6 | ASTM D882A | 4.83 MPa |
| MD:断裂,25µm7 | ASTM D882A | 62.1 MPa | |
| TD:断裂,25µm8 | ASTM D882A | 39.3 MPa | |
| TD:断裂,25µm9 | ASTM D882A | 18.6 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melting temperature | ASTM D3417 | 131 °C |