برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D-792 | 1.07 |
| Shrinkage rate | | ASTM D-955 | 0.003-0.007 cm/cm |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transparency | | ASTM D-1003 | 89.5 % |
| Haze ratio | | ASTM D-1003 | 0.6 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 230℃/3.8kg | ASTM D-1238 | 8.5 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服 | ASTM D-638 | 675 Kg/cm |
| tensile strength | | ASTM D-638 | 675 Kg/cm |
| elongation at break | | ASTM D-638 | 2.2 % |
| Tensile modulus | | ASTM D-638 | 34600 Kg/cm |
| bending strength | | ASTM D-790 | 1130 Kg/cm |
| Flexural modulus | | ASTM D-790 | 38000 Kg/cm |
| Impact strength of cantilever beam gap | | ASTM D-256 | 160 Kg/cm |
| Rockwell hardness | | ASTM D-785 | 125 Rscale |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Limiting Oxygen Index | | ASTM D-2863 | 19 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 未退火，1.8MPa，HDT | ASTM D-648 | 84 ℃ |
| Heat distortion temperature | 退火，0.45MPa，HDT | ASTM D-648 | 100 ℃ |
| Heat distortion temperature | 退火，1.8MPa，HDT | ASTM D-648 | 97 ℃ |
| vicat | | ASTM D-1525 | 107 ℃ |
| Linear coefficient of thermal expansion | | ASTM D-696 | 6.2E-05 cm/cm/℃ |
| combustibility | | UL 94 | HB |
| Heat distortion temperature | 未退火，0.45MPa，HDT | ASTM D-648 | 95 ℃ |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه