physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.70 % |
Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
Apparent density | | ISO 60 | 0.65 g/cm³ |
melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 6.0 g/10min |
Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 5.00 cm³/10min |
Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.55 % |
flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 930 °C |
Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 930 °C |
Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 930 °C |
Limiting Oxygen Index | | ISO 4589-2 | 36 % |
UL flame retardant rating | 6.0mm | UL 94 | V-0 |
UL flame retardant rating | 6.0mm | UL 94 | V-0 |
Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Tensile strain | 断裂,23°C | ISO 527-2/5 | 40 % |
Flexural modulus | 23°C | ISO 178 | 2900 MPa |
bending strength | 23°C | ISO 178 | 100 MPa |
Bending Strain | 23°C | ISO 178 | 6.2 % |
Tensile modulus | 23°C | ISO 527-2/1 | 3000 MPa |
tensile strength | 屈服,23°C | ISO 527-2/5 | 64.0 MPa |
tensile strength | 断裂,23°C | ISO 527-2/5 | 50.0 MPa |
Tensile strain | 屈服,23°C | ISO 527-2/5 | 5.4 % |
Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Impact strength of simply supported beam without notch | -60°C,CompleteBreak | ISO 179/1eU | 150 kJ/m² |
Impact strength of simply supported beam without notch | -30°C,完全断裂 | ISO 179/1eU | 160 kJ/m² |
Impact strength of simply supported beam without notch | 23°C,完全断裂 | ISO 179/1eU | 220 kJ/m² |
Impact strength of cantilever beam gap | 23°C,CompleteBreak | ISO 7391 | 12 kJ/m² |
Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 25.0 J |
Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 30.0 J |
Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 4900 N |
Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 4400 N |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | PLC 4 |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Linear coefficient of thermal expansion | MD:23到55°C | ISO 11359-2 | 5.5E-05 cm/cm/°C |
Linear coefficient of thermal expansion | TD:23to55°C | ISO 11359-2 | 7E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 141 °C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 132 °C |
vicat | | ISO 306/B50 | 144 °C |