| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 23℃，24hr | ISO 62 | 0.15 % |
| density | | ISO 1183 | 1.46 g/cm3 |
| processability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | | ISO 294-4 | 1.4-2.0 % |
| spiral flow length | | | -- cm |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D-792 | 1.40 g/cm |
| Shrinkage rate | | ASTM D-955 | 1.4-2.0 % |
| Water absorption rate | | ASTM D-570 | 0.10 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | | ISO 527 | 58 MPa |
| elongation | Break | ISO 527 | 18 % |
| bending strength | | ISO 178 | 90 MPa |
| Flexural modulus | | ISO 178 | 2.5*103 MPa |
| Charpy Notched Impact Strength | Notched | ISO 179（leA） | 5 KJ/m2 |
| Impact strength of cantilever beam gap | 1/8 | ASTM D-256 | 28 J/m |
| tensile strength | | ASTM D-638 | 45 MPa |
| bending strength | | ASTM D-790 | 90 MPa |
| Charpy Notched Impact Strength | 无缺口 | ISO 179 | 30 KJ/M |
| Charpy Notched Impact Strength | Notched | ISO 179 | 4 KJ/M |
| Rockwell hardness | | ASTM D-785 | 80 M scale |
| Flexural modulus | | ASTM D-790 | 2500 MPa |
| Flame retardant performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | | UL 94 | V-0（0.8mm） |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric constant | 106HZ | IEC 60250 | 3 |
| Dielectric loss | 106HZ，正切 | IEC 60250 | 2*10-2 |
| Volume resistivity | | IEC 60093 | 1*1014 Ω。m |
| dielectric strength | | IEC 60243 | 32 KV/m |
| arc resistance | | IEC 61621 | -- Sec |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Dissipation Factor | | ASTM D-150 | 2.0×10 10 |
| dielectric strength | 2mm | ASTM D-149 | 21 MV/m |
| dielectric constant | | ASTM D-150 | 3.0 10 |
| Volume resistivity | | ASTM D-257 | 10 Ω.cm |
| ash content | | | 0 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hot deformation temperature (HDT) | 1.82MPa，HDT | ISO 75f | 62 ℃ |
| 线性热膨胀系数 | -30-30℃ | ASTM D-696 | 7.0 10 |
| Hot deformation temperature (HDT) | 1.82MPa，HDT | ASTM D-648 | 80 ℃ |
| UL flame retardant rating | 1/8-1/32" | UL 94 | V-0 |