PEEK KT-850 NT
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.30 g/cm | |
| melt mass-flow rate | 2.16kg@400℃ | ASTM D1238 | 10 g/10 min |
| Water absorption rate | 24hr | ASTM D570 | 0.10 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3650 MPa | |
| tensile strength | ASTM D638 | 96.5 MPa | |
| elongation | 屈服 | ASTM D638 | 5.2 % |
| elongation at break | ASTM D638 | 20-30 % | |
| Flexural modulus | ASTM D790 | 3680 MPa | |
| bending strength | ASTM D790 | 152 MPa | |
| Impact strength of cantilever beam gap | ASTM D256 | 69.4 J/m | |
| Suspended wall beam without notch impact strength | ASTM D256 | 不断裂 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Hot deformation temperature (HDT) | 1.82MPa，未退火，HDT | ASTM D648 | 162 ℃ |
| Glass Transition Temperature | ASTM D3417 | 150 ℃ | |
| melting temperature | ASTM D3417 | 340 ℃ | |
| 线性热膨胀系数 | -50~50℃ | ASTM E831 | 0.000043 cm/cm/℃ |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.