PET UmaPET SI Ester Industries Ltd.

مقایسه

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
turbidity	23.0μm	ASTM D1003	4.5 %
	turbidity	15.0μm	ASTM D1003	3.5 %
		turbidity	12.0μm	ASTM D1003	3.5 %
		turbidity	turbidity	10.0μm	ASTM D1003	3.5 %

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Friction coefficient	Itself - Static5	ASTM D1894	0.40
	Friction coefficient	Itself - Dynamic4	ASTM D1894	0.35
		Friction coefficient	Itself - Dynamic3	ASTM D1894	0.35
			Friction coefficient	Itself - Dynamic2	ASTM D1894	0.35
				Friction coefficient	Itself - Dynamic1	ASTM D1894	0.35
					Friction coefficient	Itself - Static6	ASTM D1894	0.40
						Friction coefficient	Itself - Static7	ASTM D1894	0.40
						Friction coefficient	Friction coefficient	Itself - Static8	ASTM D1894	0.40

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	TD:150°C,30分钟,0.0230mm	ASTM D1204	0.40 %
	Shrinkage rate	TD:150°C,30分钟,0.0150mm	ASTM D1204	0.40 %
		Shrinkage rate	TD:150°C,30分钟,0.0120mm	ASTM D1204	0.40 %
			Shrinkage rate	TD:150°C,30分钟,0.0100mm	ASTM D1204	0.40 %
				Shrinkage rate	MD:150°C,30分钟,0.0230mm	ASTM D1204	2.5 %
					Shrinkage rate	MD:150°C,30分钟,0.0100mm	ASTM D1204	2.5 %
						Shrinkage rate	MD:150°C,30分钟,0.0120mm	ASTM D1204	2.5 %
						Shrinkage rate	Shrinkage rate	MD:150°C,30分钟,0.0150mm	ASTM D1204	2.5 %

film	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	TD:Break,10μm	ASTM D882	216 MPa
	tensile strength	MD:Break,23μm	ASTM D882	186 MPa
		tensile strength	MD:Break,15μm	ASTM D882	186 MPa
		tensile strength	tensile strength	MD:Break,12μm	ASTM D882	206 MPa
consumption	23.0μm	Internal Method	31.0 m²/kg
	consumption	15.0μm	Internal Method	47.6 m²/kg
		consumption	12.0μm	Internal Method	59.5 m²/kg
		consumption	consumption	10.0μm	Internal Method	71.4 m²/kg
elongation	TD:Break,23μm	ASTM D882	90 %
elongation	elongation	TD:Break,15μm	ASTM D882	90 %
film thickness			10121523 µm
film thickness	film thickness			10.12.15.23µm
tensile strength	MD:Break,10μm	ASTM D882	206 MPa
elongation	MD:Break,15μm	ASTM D882	100 %
	elongation	MD:Break,23μm	ASTM D882	100 %
		elongation	TD:Break,10μm	ASTM D882	90 %
		elongation	elongation	TD:Break,12μm	ASTM D882	90 %
tensile strength	TD:Break,12μm	ASTM D882	216 MPa
	tensile strength	TD:Break,15μm	ASTM D882	206 MPa
	tensile strength	tensile strength	TD:Break,23μm	ASTM D882	206 MPa
elongation	MD:Break,10μm	ASTM D882	100 %
elongation	elongation	MD:Break,12μm	ASTM D882	100 %

Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
viscosity	10.0μm	Internal Method	Pass
	viscosity	12.0μm	Internal Method	Pass
		viscosity	15.0μm	Internal Method	Pass
		viscosity	viscosity	23.0μm	Internal Method	Pass
Surface electrostatic charge	10.0μm	Internal Method	Nil
	Surface electrostatic charge	12.0μm	Internal Method	Nil
		Surface electrostatic charge	15.0μm	Internal Method	Nil
		Surface electrostatic charge	Surface electrostatic charge	23.0μm	Internal Method	Nil
wetting tension	10.0μm，平面 (Plainside)	ASTM D2578	44 dyne/cm
	wetting tension	12.0μm，平面 (Plainside)	ASTM D2578	44 dyne/cm
		wetting tension	15.0μm，平面 (Plainside)	ASTM D2578	44 dyne/cm
		wetting tension	wetting tension	23.0μm，平面 (Plainside)	ASTM D2578	44 dyne/cm