برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 2.00 cm3/10min |
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.60-0.80 % |
| Melt volume flow rate | 220℃/2.16 kg | ISO 1133 | 2.00 cm3/10min |
| Shrinkage rate | MD，23℃ | ISO 294-4 | 0.60 - 0.80 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 100 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2 | 2150 Mpa |
| tensile strength | 23°C | ISO 527-2 | 40.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2230 Mpa |
| bending strength | 23°C | ISO 178 | 65.0 Mpa |
| tensile strength | 23℃ | ISO 527-2 | 40.0 Mpa |
| Flexural modulus | 23℃ | ISO 178 | 2230 Mpa |
| bending strength | 23℃ | ISO 178 | 65.0 Mpa |
| Charpy Notched Impact Strength | -30℃ | ISO 179 | 3.0 kJ/m² |
| Rockwell hardness | 23℃ | ISO 2039-2 | 100 R 计秤 |
| Tensile modulus | 23℃ | ISO 527-2 | 2150 Mpa |
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 3 kg·cm/cm(J/M)ft·lb/in |
| Tensile modulus | | ASTM D638/ISO 527 | 2150 kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D638/ISO 527 | 40 kg/cm²(MPa)[Lb/in²] |
| Rockwell hardness | | ASTM D785 | 100 |
| Flexural modulus | | ASTM D790/ISO 178 | 2230 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 65 kg/cm²(MPa)[Lb/in²] |
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 6 kg·cm/cm(J/M)ft·lb/in |
| Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792/ISO 1183 | 1.21 |
| Shrinkage rate | | ASTM D955 | 0.6-0.8 % |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 2 g/10min |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 105 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 1.80MPa，未退火，HDT | ISO 75-2/Af | 105 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 0.000080 cm/cm/℃ |
| UL flame retardant rating | | UL 94 | V-0 |
| Combustibility (rate) | | UL 94 | 1.5 V-0 |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 105 ℃（℉） |
| Linear coefficient of thermal expansion | | ASTM D696/ISO 11359 | 8 mm/mm.℃ |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.