برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 295°C/6.6kg | ASTM D1238 | 7.0 g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.87-0.92 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.76 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | 邵氏D | ASTM D2240 | 80 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| Limiting Oxygen Index | | ASTM D2863 | 48 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 断裂 | ISO 527-2/50 | 59.0 Mpa |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.0 % |
| elongation | 断裂 | ASTM D638 | 20 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 15 % |
| Flexural modulus | -- | ASTM D790 | 2150 Mpa |
| Flexural modulus | 50.0mm跨距4 | ASTM D790 | 2150 Mpa |
| Flexural modulus | | ISO 178 | 2000 Mpa |
| bending strength | | ASTM D790 | 94.0 Mpa |
| bending strength | | ISO 178 | 98.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 94.0 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 50.0 mg |
| Tensile modulus | | ASTM D638 | 2400 Mpa |
| Tensile modulus | | ISO 527-2/1 | 2300 Mpa |
| tensile strength | 屈服 | ASTM D638 | 62.0 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 68.0 Mpa |
| tensile strength | 断裂 | ASTM D638 | 53.0 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 16 kJ/m² |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tear strength | 1.60mm | ISO 34-1 | 37 kN/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dissipation Factor | 1MHz | ASTM D150 | 5.4E-03 |
| Surface Resistivity | | ASTM D257 | >1.0E+15 ohms |
| Volume resistivity | | ASTM D257 | >1.0E+16 ohms·cm |
| dielectric strength | 3.20mm,inOil | ASTM D149 | 17 KV/mm |
| dielectric constant | 100Hz | ASTM D150 | 3.13 |
| dielectric constant | 100kHz | ASTM D150 | 3.07 |
| dielectric constant | 1MHz | ASTM D150 | 3.04 |
| Dissipation Factor | 100Hz | ASTM D150 | 0.011 |
| Dissipation Factor | 100kHz | ASTM D150 | 6.1E-03 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 164 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 145 °C |
| Glass Transition Temperature | | DSC | 200 °C |
| vicat | | ISO 306/B120 | 180 °C |