machinability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate		ASTM D-570	0.15	%
Basic Performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
melt mass-flow rate		ASTM D-1238	10.5	g/10min
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Break点	ASTM D-638	69	Mpa
Bending modulus		ASTM D-790	2343	Mpa
tensile strength	屈伏点	ASTM D-638	62	Mpa
Impact strength of cantilever beam gap	Notched23℃	ASTM D-256	800	J/m
Elongation at Break	Break点	ASTM D-638	130	%
bending strength		ASTM D-790	96	Mpa
Rockwell hardness	R	ASTM D-785	118
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Long term use temperature		UL 746B	130	°C
UL flame retardant rating		UL 94	HB
Vicat softening temperature		ASTM D-1525	154	°C
UL flame retardant rating		UL 94	1.1	mm
Hot deformation temperature	0.45MPa	ASTM D-648	137	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa	ASTM D-648	132	°C
Linear coefficient of thermal expansion		ASTM E-831	6.8×10	1/℃
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ASTM D-792	1.2
Shrinkage rate	3.2mm	ASTM D-955	5-7	10
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dielectric constant	60Hz	ASTM D-150	3.17
Volume resistivity		ASTM D-257	1.0×10	Ω.cm
Dielectric constant	1MHz	ASTM D-150	2.96
Dissipation factor	60Hz	ASTM D-150	0.0009
Dissipation factor	Dissipation factor	1MHz	ASTM D-150	0.01