برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.50to1.70 g/cm³ |
| Apparent density | | ISO 60 | 0.55to0.75 g/cm³ |
| Shrinkage rate | MD：--1 | ISO 2577 | 0.50to1.0 % |
| Shrinkage rate | MD：--2 | ISO 2577 | 0.80to1.3 % |
| Water absorption rate | 23°C,24hr | ISO 62 | <2.0 % |
| Shrinkage rate | | ISO 2577 | 1.0to1.5 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 900 °C |
| UL flame retardant rating | 1.50mm | UL 94 | V-0 |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compression molding pressure | | | >20.0 MPa |
| Compression molding temperature | | | 160to180 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | Compression Molded | ISO 527-2 | 5000to8000 MPa |
| Tensile modulus | Injection | ISO 527-2 | 5000to8000 MPa |
| tensile strength | CompressionMolded | ISO 527-2 | 45.0to65.0 MPa |
| Flexural modulus | Compression Molded | ISO 178 | 8000to9000 MPa |
| Flexural modulus | Injection | ISO 178 | 8000to9000 MPa |
| bending strength | Compression Molded | ISO 178 | 90.0to120 MPa |
| bending strength | Injection | ISO 178 | 100to130 MPa |
| compression stress | | ISO 604 | 200to250 MPa |
| tensile strength | InjectionMolded | ISO 527-2 | 50.0to90.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO 179/1eA | 1.4to2.0 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO 179/1eA | 1.5to2.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO 179/1eU | 6.0to9.0 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO 179/1eU | 8.0to14 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric strength | | IEC 60243-1 | 15to20 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 16.011.0 |
| relative permittivity | 1MHz | IEC 60250 | 9.007.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.30to0.50 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.030to0.050 |
| arc resistance | | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Surface Resistivity | | IEC 60093 | 1.0E+10到1.0E+11 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+11到1.0E+12 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：50到100°C | ISO 11359-2 | 1.5E-5到3.5E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40to0.50 W/m/K |
| maximum service temperature | <50h | IEC 60216 | 160 °C |
| maximum service temperature | 20,000h | IEC 60216 | 135 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.