| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 12.0 cm³/10min |
| Shrinkage rate | TD:260°C,3.00mm | ISO 2577 | 0.25to0.45 % |
| Shrinkage rate | MD:260°C,3.00mm | ISO 2577 | 0.30to0.50 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.50 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| MeltViscosity | 260°C | ISO 11443-A | 240 Pa·s |
| density | 23°C | ISO 1183 | 1.29 g/cm³ |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.9mm | UL 94 | HB |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 20 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/A | 6.0 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180 | 50 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 100 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile strain | 断裂,23°C | ISO 527-2/50 | 9.0 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 4900 MPa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 60.0 MPa |
| tensile strength | 断裂,23°C | ISO 527-2/50 | 50.0 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 3.2 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
| Surface Resistivity | | IEC 60093 | 1E+16 ohms |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 35 kV/mm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.30 |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.20 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 1.5E-03 |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 3.2E-03 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 127 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 111 °C |
| vicat | -- | ISO 306/B50 | 128 °C |
| vicat | -- | ISO 306/B120 | 130 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 5.6E-05 cm/cm/°C |