برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 8.50 cm3/10min |
| Shrinkage rate | MD3 | 内部方法 | 0.40-0.60 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.32 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.13 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 100 Mpa |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| refractive index | | ISO 489 | 1.586 |
| transmissivity | 2540µm | ASTM D1003 | 88.0to90.0 % |
| Haze ratio | 2540µm | ASTM D1003 | <0.80 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| UL flame retardant rating | 2.5mm | UL 94 | V-0 |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 850 °C |
| Burning wire flammability index | 1.8mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 40 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| Flexural modulus | | ISO 178 | 2300 Mpa |
| bending strength | | ISO 178 | 95.0 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 9.00 mg |
| Tensile modulus | | ISO 527-2/1 | 2350 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 70.0 Mpa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 35 KV/mm |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 27 KV/mm |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm |
| relative permittivity | 50Hz | IEC 60250 | 2.70 |
| relative permittivity | 60Hz | IEC 60250 | 2.70 |
| relative permittivity | 1MHz | IEC 60250 | 2.70 |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| Dissipation Factor | 60Hz | IEC 60250 | 1E-03 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| thermal conductivity | | ISO 8302 | 0.20 W/m/K |
| RTI Elec | | UL 746 | 80.0 °C |
| RTI Imp | | UL 746 | 80.0 °C |
| RTI | | UL 746 | 80.0 °C |
| Heat distortion temperature | 0.45MPa,未退火,100mm跨距，HDT | ISO 75-2/Be | 140 °C |
| Heat distortion temperature | 1.8MPa,未退火,100mm跨距，HDT | ISO 75-2/Ae | 129 °C |
| vicat | -- | ISO 306/B50 | 144 °C |
| vicat | -- | ISO 306/B120 | 145 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |
| ball-indentation hardness | 140°C9 | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.