برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |
| other | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| characteristic | | | 滚塑成型 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| gloss | 45° | ASTM D2457 | 61 |
| Haze ratio | | ASTM D1003 | 7.1 % |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Secant modulus | 1%正割,MD | ASTM D882 | 205 Mpa |
| Secant modulus | 1%正割,TD | ASTM D882 | 230 Mpa |
| tensile strength | MD:屈服 | ASTM D882 | 9.64 Mpa |
| tensile strength | TD:屈服 | ASTM D882 | 10.4 Mpa |
| tensile strength | MD:断裂 | ASTM D882 | 57.5 Mpa |
| tensile strength | TD:断裂 | ASTM D882 | 53.1 Mpa |
| elongation | MD:断裂 | ASTM D882 | 520 % |
| elongation | TD:断裂 | ASTM D882 | 730 % |
| Dart impact | | ASTM D1709A | 190 g |
| Elmendorf tear strength | MD | ASTM D1922 | 120 g |
| Elmendorf tear strength | TD | ASTM D1922 | 560 g |
| Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792/ISO 1183 | 0.985-1.0 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 130-142 g/10min |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 85 ℃（℉） |