Basic Performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melt Volume Flow Rate (MVR)	230°C/2.16 kg	ISO 1133	10	CM
melt mass-flow rate	230°C/2.16 kg	ISO 1133	7.5	g/10min
density		ISO 1183	0.9
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shore hardness		ISO 2039-1	64
Impact strength of simply supported beam without notch	23℃	ISO 179	133
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23℃	ISO 179	3.5
Tensile strain	Break	ISO 527-1	50	%
Tensile strain	Tensile strain	Yield	ISO 527-1	10	%
tensile strength	Yield	ISO 527-1	31	Mpa
Tensile modulus		ISO 527-1	1400	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Vicat softening temperature	B50 (50°C/h 10N)	ISO 306	82	°C
Vicat softening temperature	Vicat softening temperature	A50 (50°C/h 10N)	ISO 306	152	°C
Hot deformation temperature	0.45Mpa, Unannealed	ISO 75B-1	83	°C
Hot deformation temperature	Hot deformation temperature	0.45Mpa, Unannealed	ASTM D648	83	°C