برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D1505 | 0.910 g/cm³ |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 12 g/10min |
| Shrinkage rate | MD:2.00mm | ASTM D955 | 1.2 % |
| Shrinkage rate | TD:2.00mm | ASTM D955 | 1.2 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 90 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| gloss | | ASTM D2457 | 51 |
| Haze ratio | | ASTM D1003 | 47 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Yield | ASTM D638 | 31.4 MPa |
| tensile strength | Break | ASTM D638 | 19.6 MPa |
| elongation | Break | ASTM D638 | 650 % |
| Flexural modulus | | ASTM D790 | 15500 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 0°C | ASTM D256 | 20 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 29 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | | ASTM D1525 | 155 °C |
| melting temperature | | ASTM D2117 | 163 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 110 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 65.0 °C |
| brittle temperature | | ASTM D746 | -20.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه