برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.15 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 3.17mm | ASTM D256 | 800 J/m |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | 断裂,3.17mm | ASTM D638 | 110 % |
| Flexural modulus | 3.17mm | ASTM D790 | 2070 MPa |
| bending strength | 屈服,3.17mm | ASTM D790 | 86.2 MPa |
| tensile strength | 屈服,3.17mm | ASTM D638 | 55.2 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| arc resistance | | ASTM D495 | 60.0to120 sec |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 1.50mm | UL 746 | PLC 0 |
| High arc combustion index (HAI) | 3.00mm | UL 746 | PLC 0 |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 0 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 mm/min |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | 1.50mm | UL 746 | PLC 2 sec |
| Hot wire ignition (HWI) | 3.00mm | UL 746 | PLC 1 sec |
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 127 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 137 °C |
| RTI | | UL 746 | 125 °C |
| Linear coefficient of thermal expansion | MD:-40到95°C | ASTME831 | 7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD:-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| RTI Elec | | UL 746 | 125 °C |
| RTI Imp | | UL 746 | 115 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.