| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | -- | ASTM D792 | 1.19 g/cm³ |
| Specific volume | | ASTM D792 | 0.835 cm³/g |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 18 g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.35 % |
| Water absorption rate | 平衡,100°C | ASTM D570 | 0.58 % |
| Outdoor applicability | | UL 746C | f1 |
| density | -- | ASTM D792 | 1.20 g/cm³ |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 70 |
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| refractive index | | ASTM D542 | 1.586 |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.762mm | UL 94 | HB |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dart impact | 23°C | ASTM D3029 | 169 J |
| Impact strength of cantilever beam gap | | ASTM D1822 | 546 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 690 J/m |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Yield | ASTM D638 | 62.1 MPa |
| tensile strength | Break | ASTM D638 | 65.5 MPa |
| elongation | Yield | ASTM D638 | 7.0 % |
| elongation | Break | ASTM D638 | 110 % |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 MPa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 93.1 MPa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | >1.0E+17 ohms·cm |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 15 kV/mm |
| dielectric constant | 50Hz | ASTM D150 | 3.17 |
| dielectric constant | 60Hz | ASTM D150 | 3.17 |
| dielectric constant | 1MHz | ASTM D150 | 2.96 |
| Dissipation Factor | 50Hz | ASTM D150 | 9E-04 |
| Dissipation Factor | 60Hz | ASTM D150 | 9E-04 |
| Dissipation Factor | 1MHz | ASTM D150 | 0.010 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 4 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| RTI | | UL 746 | 100 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 138 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 132 °C |
| vicat | | ASTM D15256 | 154 °C |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| specific heat | | ASTMC351 | 1260 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.19 W/m/K |
| RTI Elec | | UL 746 | 100 °C |
| RTI Imp | | UL 746 | 100 °C |