impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	65	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	60	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	75	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	55	kJ/m²
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
bending strength	23°C	ISO 178	245	Mpa
Bending modulus	23°C	ISO 178/A	8500	Mpa
Tensile strain	Break,23°C	ISO 527-2/5	3.5	%
tensile strength	Break,23°C	ISO 527-2/5	145	Mpa
Tensile modulus	23°C	ISO 527-2/1	9200	Mpa
Bending strain	23°C		3.3	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2E-05	cm/cm/°C
Melting temperature		ISO 11357-3	220	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	210	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.050	%
	Shrinkage rate	MD:280°C,2.00mm2	ISO 294-4	0.25	%
		Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.090	%
		Shrinkage rate	Shrinkage rate	TD:280°C,2.00mm2	ISO 294-4	0.75	%
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
ISO Shortcut		ISO 1874	PA6-HI.GR.14-100.GF30