ABS TR-7 MITSUBISHI RAYON AMERICA
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D-792 | 1.06 g/cm | |
| Shrinkage rate | Flow | ASTM D-955 | 0.55 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 200℃/5.0kg | ASTM D-1238 | 0.30 g/10min |
| Water absorption rate | 24hr | ASTM D-570 | 0.30 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| bending strength | 23℃，6.35mm，屈服 | ASTM D-790 | 72.6 MPa |
| Impact strength of cantilever beam gap | -40℃，6.35mm | ASTM D-256 | 39.2 J/m |
| Rockwell hardness | ASTM D-785 | 110 R-Scale | |
| Tensile modulus | 23℃ | ASTM D-638 | 2450 MPa |
| tensile strength | 屈服,23℃ | ASTM D-638 | 47.1 MPa |
| Flexural modulus | 23℃，6.35mm | ASTM D-790 | 2450 MPa |
| Impact strength of cantilever beam gap | 0℃，6.35mm | ASTM D-256 | 68.6 J/m |
| 23℃，6.35mm | ASTM D-256 | 98.1 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa，未退火，12.7mm，HDT | ASTM D-648 | 110 ℃ |
| Linear coefficient of thermal expansion | Flow | ASTM D-696 | 0.000090 cm/cm/℃ |
| specific heat | ASTM C-351 | 1670 J/kg/℃ | |
| thermal conductivity | ASTM C-177 | 0.21 W/m.K | |
| UL flame retardant rating | NC | UL 94 | HB |