ABS XANTAR® C CP 200 Mitsubishi Chemical Corporation

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	23°C	ISO 180/4A	50 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-2	2000 MPa
tensile strength	Yield	ISO 527-2	45.0 MPa
Tensile strain	Yield	ISO 527-2	4.5 %
Nominal tensile fracture strain		ISO 527-2	>50 %
Bending modulus		ISO 178	1800 MPa
bending strength		ISO 178	67.0 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	95.0 °C
Vicat softening temperature		ISO 306/B50	112 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	9E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	9E-05 cm/cm/°C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	260°C/5.0kg	ISO 1133	26 g/10min
Shrinkage rate	MD	ISO 294-4	0.60 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.70 %
density		ISO 1183	1.10 g/cm³

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.