TPE DuraGrip® DGR 6080NC USA Advanced

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tear strength	24°C	ASTM D624	33.4	kN/m
elongation	Break,23°C	ISO 37	310	%
elongation	elongation	Break	ASTM D412	310	%
tensile strength	Yield,23°C	ISO 37	8.30	MPa
tensile strength	tensile strength	Yield,23°C	ASTM D412	8.30	MPa
Permanent compression deformation	100°C,22hr	ISO 815	63	%
	Permanent compression deformation	24°C,22hr	ASTM D395B	26	%
		Permanent compression deformation	70°C,22hr	ISO 815	48	%
			Permanent compression deformation	24°C,22hr	ISO 815	26	%
				Permanent compression deformation	100°C,22hr	ASTM D395B	63	%
				Permanent compression deformation	Permanent compression deformation	70°C,22hr	ASTM D395B	48	%
Stretch permanent deformation	100%Strain	ASTM D412	16	%
tensile strength	100%Strain	ASTM D412	2.54	MPa
tensile strength	tensile strength	100%Strain,23°C	ISO 37	2.54	MPa
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Taber wear resistance	1000Cycles,1.0E+6g,CS-17Wheel	ASTM D1044	12.5	mg
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Brittle temperature		ISO 812	-61.1	°C
Brittle temperature	Brittle temperature		ASTM D746	-61.1	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ISO 1183	0.988	g/cm³
Shrinkage rate	MD：1.59mm	ASTM D955	1.4	%
density		ASTM D792	0.988	g/cm³
Shrinkage rate	MD：3.18mm	ASTM D955	1.3	%
	Shrinkage rate	TD：1.59mm	ASTM D955	0.50	%
		Shrinkage rate	TD：3.18mm	ASTM D955	1.1	%
			Shrinkage rate	TD:1.59mm	ISO 294-4	0.50	%
				Shrinkage rate	MD:1.59mm	ISO 294-4	1.4	%
					Shrinkage rate	TD:3.18mm	ISO 294-4	1.1	%
					Shrinkage rate	Shrinkage rate	MD:3.18mm	ISO 294-4	1.3	%
MeltViscosity	190°C,300sec^-1	ASTM D3835	219	Pa·s
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shore hardness	ShoreA,5Sec	ISO 868	78
Shore hardness	Shore hardness	ShoreA,5Sec	ASTM D2240	78
aging	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume change	24°C,168hr,inReferenceFuelB	ISO 1817	54	%
	Volume change	100°C,168hr,在水中	ASTM D471	1.0	%
		Volume change	100°C,168hr,inIRM903Oil	ASTM D471	82	%
			Volume change	100°C,168hr,inASTM#1Oil	ASTM D471	6.0	%
			Volume change	Volume change	24°C,168hr,inReferenceFuelB	ASTM D471	54	%
Tensile stress change rate	100°C,168hr，Break	ISO 1817	4.0	%
Tensile stress change rate	Tensile stress change rate	70°C,168hr，Break	ISO 1817	-5.0	%
Change rate of ultimate elongation in air	100°C,168hr	ASTM D573	4.0	%
Change rate of tensile strength in air	100%Strain,70°C,168hr	ASTM D573	7.0	%
	Change rate of tensile strength in air	70°C,168hr	ASTM D573	-2.0	%
		Change rate of tensile strength in air	100°C,168hr	ASTM D573	-2.0	%
			Change rate of tensile strength in air	100%Strain,100°C,168hr	ASTM D573	7.0	%
				Change rate of tensile strength in air	70°C,168hr	ISO 188	-2.0	%
					Change rate of tensile strength in air	100°C,168hr	ISO 188	-2.0	%
					Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain100°C,168hr	ISO 188	7.0	%
Change rate of ultimate elongation in air	70°C,168hr	ASTM D573	-5.0	%
Volume change	100°C,168hr,inASTM#1Oil	ISO 1817	6.0	%
	Volume change	100°C,168hr,inIRM903Oil	ISO 1817	82	%
	Volume change	Volume change	100°C,168hr,在水中	ISO 1817	1.0	%
Change rate of tensile strength in air	100%Strain70°C,168hr	ISO 188	7.0	%