PPO(PPE)+PS Generic PPE+PS Generic

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

Filling analysis	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melt viscosity		ASTM D3835	66.0to100	Pa·s
impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dart impact	23°C	ASTM D3029	13.6to17.2	J
Charpy Notched Impact Strength	23°C	ISO 179	5.3to21	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	17to150	kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	31to380	J/m
	Impact strength of cantilever beam gap	23°C	ISO 180	3.8to26	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	7.00to18.0	kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D256	160to2600	J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180	17to180	kJ/m²
Dart impact	23°C	ASTM D3763	9.03to54.8	J
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Burning wire flammability index		IEC 60695-2-12	952to960	°C
Hot filament ignition temperature		IEC 60695-2-13	697to960	°C
Extreme Oxygen Index	--	ASTM D2863	22to39	%
Extreme Oxygen Index	Extreme Oxygen Index	--	ISO 4589-2	20to34	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Break,23°C	ISO 527-2	35.0to80.9	MPa
tensile strength	tensile strength	23°C	ASTM D638	39.6to70.0	MPa
elongation	Yield,23°C	ASTM D638	2.0to5.3	%
	elongation	Yield,23°C	ISO 527-2	1.7to5.1	%
		elongation	Break,23°C	ASTM D638	1.7to83	%
		elongation	elongation	Break,23°C	ISO 527-2	3.3to31	%
Nominal tensile fracture strain	23°C	ISO 527-2	9.0to31	%
Bending modulus	23°C	ASTM D790	1920to2840	MPa
Bending modulus	Bending modulus	23°C	ISO 178	1920to3050	MPa
bending strength	23°C	ASTM D790	53.1to111	MPa
	bending strength	23°C	ISO 178	57.5to113	MPa
		bending strength	Yield,23°C	ASTM D790	52.4to155	MPa
		bending strength	bending strength	Break,23°C	ASTM D790	47.6to136	MPa
Friction coefficient		ASTM D1894	0.19to0.28
Taber abraser	23°C	ASTM D1044	35.0to78.9	mg
Tensile modulus	23°C	ASTM D638	2040to2890	MPa
Tensile modulus	Tensile modulus	23°C	ISO 527-2	2170to2700	MPa
tensile strength	Yield,23°C	ASTM D638	32.7to81.7	MPa
	tensile strength	Yield,23°C	ISO 527-2	35.8to76.4	MPa
	tensile strength	tensile strength	Break,23°C	ASTM D638	38.5to62.4	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	87.6to161	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	95.0to160	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	72.6to150	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0to148	°C
RTI		UL 746	50.0to112	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	6.6E-5到9.4E-5	cm/cm/°C
	Linear coefficient of thermal expansion	TD	ASTME831	5.5E-5到9.6E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	5.6E-5到9.5E-5	cm/cm/°C
thermal conductivity	23°C	ISO 8302	0.18to0.27	W/m/K
RTI Elec		UL 746	50.0to112	°C
RTI Imp		UL 746	50.0to106	°C
Vicat softening temperature	--	ASTM D1525	94.4to168	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306	91.0to164	°C
Linear coefficient of thermal expansion	MD	ASTME831	5.9E-5到9.5E-5	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	23°C,24hr	ISO 62	0.059to0.10	%
	Water absorption rate	Saturation,23°C	ISO 62	0.060to0.25	%
	Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.045to0.067	%
density	23°C	ISO 1183	1.03to1.12	g/cm³
melt mass-flow rate	280°C/5.0kg	ASTM D1238	1.3to18	g/10min
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	5.70to18.6	cm³/10min
Shrinkage rate	MD:23°C	ASTM D955	0.59to0.61	%
	Shrinkage rate	TD:23°C	ASTM D955	0.56to0.60	%
	Shrinkage rate	Shrinkage rate	23°C	ISO 294-4	0.58to0.61	%
Water absorption rate	23°C,24hr	ASTM D570	0.054to0.10	%
density	--	ASTM D792	1.05to1.11	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity	--	IEC 60093	2.0E+3到3.1E+16	ohms
Volume resistivity	23°C	ASTM D257	1.0E+3到3.8E+16	ohms·cm
Volume resistivity	Volume resistivity	23°C	IEC 60093	1.0E+15到3.9E+16	ohms·cm
Dielectric strength	23°C	ASTM D149	17to36	kV/mm
Dielectric strength	Dielectric strength	23°C	IEC 60243-1	15to35	kV/mm
Dielectric constant	23°C	ASTM D150	2.51to2.91
	Dielectric constant	23°C	IEC 60250	2.80to2.90
	Dielectric constant	Dielectric constant	23°C	IEC 60250	2.70
Dissipation factor	23°C	ASTM D150	4.0E-4到0.067
Dissipation factor	Dissipation factor	23°C	IEC 60250	4.0E-4到4.1E-3
Compared to the anti leakage trace index		IEC 60112	PLC 2
Surface resistivity	--	ASTM D257	5.1E+3到3.1E+16	ohms
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	23°C	ASTM D785	113to124
Ball Pressure Test		ISO 2039-1	70.0to114	MPa