| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 112 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Haze ratio | | ASTM D1003 | <1.0 % |
| transmissivity | 总计 | ASTM D1003 | 90.0 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | 屈服,23°C | ASTM D638 | 6.0 % |
| Tensile strain | 屈服,23°C | ISO 527-2 | 7.0 % |
| elongation | 断裂,23°C | ASTM D638 | 210 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 190 % |
| Flexural modulus | 23°C | ASTM D790 | 1550 Mpa |
| Flexural modulus | 23°C | ISO 178 | 1500 Mpa |
| bending strength | 23°C | ISO 178 | 59.0 Mpa |
| bending strength | 屈服,23°C | ASTM D790 | 62.0 Mpa |
| Tensile modulus | 23°C | ASTM D638 | 1550 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 1550 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 43.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 43.0 Mpa |
| tensile strength | 断裂,23°C | ASTM D638 | 53.0 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 58.0 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dart impact | -40°C,EnergyatPeakLoad | ASTM D3763 | 66.0 J |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 61.0 J |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 99.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 85.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.