| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.79 g/cm³ |
| Apparent density | | ASTM D1895 | 0.30 g/cm³ |
| Shrinkage rate | MD | ASTM D955 | 0.15to0.35 % |
| Water absorption rate | | ASTM D570 | 0.32 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Limiting Oxygen Index | | ASTM D2863 | 30 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flexural modulus | | ASTM D790 | 13800 MPa |
| bending strength | | ASTM D790 | 125 MPa |
| compressive strength | | ASTM D695 | 187 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | | ASTM D256A | 52 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 0 |
| dielectric strength | | ASTM D149 | 17 kV/mm |
| dielectric constant | 1MHz | ASTM D150 | 4.30 |
| Dissipation Factor | 1MHz | ASTM D150 | 0.016 |
| arc resistance | | ASTM D495 | 133 sec |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD | ASTME831 | 2.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648A | 260 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ASTM D648A | >280 °C |
| thermal conductivity | | ASTMC518 | 0.31 W/m/K |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.