physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
melt mass-flow rate | | ASTM D1238 | 35 g/10min |
average molecular weight | | 内部方法 | 231000 Mw |
Shrinkage rate | MD | ASTM D955 | 0.80to2.3 % |
Water absorption rate | Saturation | ASTM D750 | 0.54 % |
hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Shore hardness | 邵氏D | ASTM D2240 | 56 |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
tensile strength | 100%应变 | ASTM D1708 | 18.1 MPa |
tensile strength | 300%应变 | ASTM D1708 | 49.0 MPa |
elongation | Break | ASTM D1708 | 370 % |
Flexural modulus | | ASTM D790 | 95.1 MPa |
bending strength | 5.0%应变 | ASTM D790 | 3.52 MPa |
coefficient of friction | Itself - Dynamic | ASTM D1894 | 0.46 |
Taber abraser | 1000Cycles,1000g,H-18转轮 | ASTM D1044 | 11.0 mg |
tensile strength | Break | ASTM D1708 | 61.8 MPa |
tensile strength | 50%应变 | ASTM D1708 | 13.6 MPa |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
dielectric strength | | ASTM D149 | 17 kV/mm |
dielectric constant | 60Hz | ASTM D150 | 3.71 |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Glass Transition Temperature | | ASTME1356 | 1.00 °C |
vicat | | ASTM D1525 | 107 °C |
melting temperature | | ASTME1356 | 180 °C |