SEBS G G401.A55.B ELASTRON TURKEY
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 0.890 g/cm³ | |
| Shrinkage rate | MD | ASTM D955 | 2.8 % |
| TD | ASTM D955 | 1.4 % | |
| density | ASTM D792 | 0.890 g/cm³ | |
| Shrinkage rate | MD | ASTM D955 | 2.8 % |
| TD | 1.4 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | Shore A | ASTM D2240 | 55 |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| ozone resistance | Stressed | ASTM D518 | NoCracks |
| Stressed | ASTM D518 | No Cracks |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tear strength | ASTM D624 | 37.0 kN/m | |
| wear resistance | ASTM D1630 | 85 mm³ | |
| Shore hardness | 邵氏 A | ASTM D2240 | 55 |
| wear resistance | ASTM D1630 | 85 mm³ | |
| tensile strength | 100%应变 | ASTM D412 | 1.60 MPa |
| 300%应变 | 2.80 | ||
| Break | ASTM D412 | 6.50 MPa | |
| elongation | Break | ASTM D412 | 750 % |
| compression set | 23℃, 22.0 hr | ASTM D395 | 22 % |
| 70℃, 22.0 hr | 38 | ||
| 100℃, 22.0 hr | 64 |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 100%应变 | ASTM D412 | 1.60 MPa |
| 300%应变 | ASTM D412 | 2.80 MPa | |
| Break | ASTM D412 | 6.50 MPa | |
| elongation | Break | ASTM D412 | 750 % |
| tear strength | ASTM D624 | 37.0 kN/m | |
| compression set | 23°C,22hr | ASTM D395 | 22 % |
| 70°C,22hr | ASTM D395 | 38 % | |
| 100°C,22hr | ASTM D395 | 64 % |