PA66 Vydyne® 75HF
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ISO 1183 | 1.14 g/cm³ | |
| Water absorption rate | 饱和,23°C | ISO 62 | 8.5 % |
| 平衡,23°C,50%RH | ISO 62 | 2.5 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 断裂,23°C | ISO 527-2 | 50.0 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 5.0 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | >200 % |
| Flexural modulus | 23°C | ISO 178 | 2200 MPa |
| bending strength | 23°C | ISO 178 | 70.0 MPa |
| Poisson's ratio | ISO 527-2 | 0.40 | |
| Tensile modulus | 23°C | ISO 527-2 | 2700 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 80.0 MPa |
| Ultimate2 | ASTM D882 | 105 MPa | |
| Ultimate3 | ASTM D882 | 123 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 8.0 kJ/m² |
| 23°C | ISO 180 | 4.0 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 8.0 kJ/m² |
| 23°C | ISO 179/1eA | 4.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Secant modulus | CastFilm | ASTM D882 | 392 MPa |
| CastFilm | ASTM D882 | 444 MPa | |
| tensile strength | Break,CastFilm | ASTM D882 | 121 MPa |
| Tensile strain | Yield,CastFilm，MD | ASTM D882 | 7.0 % |
| Yield,CastFilm | ASTM D882 | 6.7 % | |
| tensile strength | Break,CastFilm | ASTM D882 | 105 MPa |
| Tensile strain | Break,CastFilm | ASTM D882 | 500 % |
| Dart impact | 42µm,CastFilm | ASTM D1709 | >2100 g |
| Elmendorf tear strength | 42µm,CastFilm，MD | ASTM D1922 | 100 g |
| 42µm,CastFilm，TD | ASTM D1922 | 110 g | |
| elongation | 断裂,挤塑薄膜 | ASTM D882 | 450 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 125 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 45.0 °C | |
| melting temperature | ISO 11357-3 | 220 °C | |
| 线性热膨胀系数 | MD：23to55°C,2.00mm | ISO 11359-2 | 1E-04 cm/cm/°C |
| TD：23to55°C,2.00mm | ISO 11359-2 | 1E-04 cm/cm/°C |