MPR 4060 NC USA Advanced

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 2781	1.17 g/cm³
density	density		ASTM D471	1.17 g/cm³
MeltViscosity	190°C,300sec^-1	ASTM D3835	400 Pa·s

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	ShoreA,1.90mm,CompressionMolded	ISO 868	57
DurometerHardness	ShoreA,1.90mm,CompressionMolded	ASTM D2240	57

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Taber abraser	1000Cycles,1000g,CS-17转轮	ASTM D1044	4.00 mg
Torsion Module	-20°C,1.90mm	ASTM D1043	6.80 MPa
Torsion Module	Torsion Module	24°C,1.90mm	ASTM D1043	1.70 MPa

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون
Stretch permanent deformation		ASTM D412	7 %
tensile strength	100%Strain,1.90mm2	ASTM D412	2.60 MPa
	tensile strength	100%Strain,125°C,1.90mm4	ASTM D573	2.50 MPa
	tensile strength	tensile strength	100%Strain,1.90mm2	ISO 37	2.60 MPa
elongation	Break,1.90mm2	ISO 37	440 %
elongation	elongation	Break,125°C,1.90mm4	ISO 188	400 %
tear strength	1.90mm	ASTM D624	29.7 kN/m
compression set	24°C,22hr	ASTM D395B	16 %
	compression set	100°C,22hr	ASTM D395B	72 %
		compression set	24°C,22hr	ISO 815	16 %
		compression set	compression set	100°C,22hr	ISO 815	72 %
Clash Mountain Module	-40°C	ASTM D1043	68.9 MPa
tensile strength	100%Strain,125°C,1.90mm4	ISO 188	2.50 MPa
	tensile strength	Yield,1.90mm2	ASTM D412	8.40 MPa
		tensile strength	Yield,125°C,1.90mm4	ASTM D573	8.20 MPa
			tensile strength	Yield,1.90mm2	ISO 37	8.40 MPa
			tensile strength	tensile strength	Yield,125°C,1.90mm4	ISO 188	8.20 MPa
elongation	Break,125°C,1.90mm4	ASTM D573	400 %
elongation	elongation	Break,1.90mm2	ASTM D412	440 %

aging	شرایط آزمون	روش آزمون	نتیجه آزمون
volume change	100°C,168hr,inASTM#1Oil	ASTM D471	-19 %
	volume change	100°C,168hr,inIRM903Oil	ASTM D471	14 %
		volume change	100°C,168hr,在水中	ASTM D471	9.0 %
			volume change	27°C,168hr,inReferenceFuelB	ISO 1817	13 %
				volume change	100°C,168hr,inASTM#1Oil	ISO 1817	-19 %
				volume change	volume change	100°C,168hr,inIRM903Oil	ISO 1817	14 %
Hardness change rate in the air	ShoreA,125°C,168hr	ASTM D573	-3.0
Shore hardness	ShoreA,125°C,168hr	ISO 188	-3.0
volume change	27°C,168hr,inReferenceFuelB	ASTM D471	13 %
volume change	volume change	100°C,168hr,在水中	ISO 1817	9.0 %

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
brittle temperature		ASTM D746	-69.0 °C
brittle temperature	brittle temperature		ISO 812	-69.0 °C