PA6 Generic Nylon 6 - Glass BeadGlass Fiber Generic

ویژگی‌ها:

Filler glass beads glass fibers

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

ویژگی‌ها:

Filler | glass beads | glass fibers

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	23°C	ISO 179	3.0to12	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	34to46	kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	37to61	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	4.0to10	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180	30to36	kJ/m²
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	2.00to3.63	J
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	700to813	N
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Burning wire flammability index		IEC 60695-2-12	650to960	°C
Extreme Oxygen Index		ISO 4589-2	23to24	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
bending strength	23°C	ASTM D790	130to200	MPa
bending strength	bending strength	23°C	ISO 178	144to186	MPa
Tensile modulus	23°C	ASTM D638	6110to6210	MPa
Tensile modulus	Tensile modulus	23°C	ISO 527-2	4700to8890	MPa
tensile strength	Break,23°C	ASTM D638	116to125	MPa
tensile strength	tensile strength	Break,23°C	ISO 527-2	92.6to125	MPa
elongation	Break,23°C	ASTM D638	2.0to4.0	%
elongation	elongation	Break,23°C	ISO 527-2	2.4to5.0	%
Bending modulus	23°C	ASTM D790	4770to5810	MPa
Bending modulus	Bending modulus	23°C	ISO 178	4690to5870	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	200to216	°C
Vicat softening temperature		ISO 306	199to211	°C
Melting temperature	--	ISO 11357-3	222	°C
Melting temperature	Melting temperature	--	ISO 3146	220	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3.0E-5到3.8E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	9E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	180to204	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	189to192	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	MD:23°C	ASTM D955	0.39to0.61	%
Shrinkage rate	Shrinkage rate	23°C	ISO 294-4	0.28to1.3	%
Water absorption rate	Saturation,23°C	ISO 62	6.5to7.1	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.0to2.3	%
density	--	ASTM D792	1.34to1.36	g/cm³
density	density	23°C	ISO 1183	1.34to1.37	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Compared to the anti leakage trace index		IEC 60112	PLC 1
Surface resistivity		IEC 60093	1.0E+10到2.5E+14	ohms
Volume resistivity	23°C	IEC 60093	1.0E+13到2.5E+15	ohms·cm
Dielectric strength	23°C	IEC 60243-1	11to37	kV/mm
Relative permittivity	23°C	IEC 60250	4.25
Dissipation factor	23°C	IEC 60250	0.013to0.027
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test		ISO 2039-1	185	MPa