optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
transmissivity	2000μm	ISO 13468-2	89.0	%
	transmissivity	3000μm	ISO 13468-2	88.0	%
	transmissivity	transmissivity	4000μm	ISO 13468-2	>87.0	%
turbidity	3000μm	ISO 14782	<0.50	%
transmissivity	1000μm	ISO 13468-2	89.0	%
Refractive index		ISO 489	1.587
impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C,Complete Break	ISO 7391	14	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,Partial Break	ISO 7391	70	kJ/m²
Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C,Complete Break	ISO 7391	15	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,Partial Break	ISO 7391	70	kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	65.0	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	60.0	J
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	6300	N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5400	N
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
SelfIgnition		ASTM D1929	550	°C
FlashIgnitionTemperature		ASTM D1929	480	°C
Extreme Oxygen Index		ISO 4589-2	28	%
UL flame retardant rating	0.75mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
bending strength	3.5%Strain,23°C	ISO 178	74.0	Mpa
bending strength	bending strength	23°C	ISO 178	98.0	Mpa
Bending strain	23°C	ISO 178	7.0	%
Tensile modulus	23°C	ISO 527-2/1	2400	Mpa
tensile strength	Yield,23°C	ISO 527-2/50	67.0	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2/50	70.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	6.1	%
Tensile strain	Tensile strain	Break,23°C	ISO 527-2/50	130	%
Bending modulus	23°C	ISO 178	2400	Mpa
Tensile creep modulus	1000hr	ISO 899-1	1900	Mpa
Tensile creep modulus	Tensile creep modulus	1hr	ISO 899-1	2200	Mpa
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	136	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	123	°C
Glass transition temperature		ISO 11357-2	144	°C
Vicat softening temperature	--	ISO 306/B50	143	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	144	°C
Ball Pressure Test	135°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
RTI Str	1.5mm	UL 746	125	°C
RTI Imp	1.5mm	UL 746	115	°C
RTI Elec	1.5mm	UL 746	125	°C
thermal conductivity	23°C	ISO 8302	0.20	W/m/K
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density	23°C	ISO 1183	1.20	g/cm³
Apparent density		ISO 60	0.66	g/cm³
melt mass-flow rate	300°C/1.2kg	ISO 1133	13	g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	12.0	cm3/10min
Shrinkage rate	TD	ISO 2577	0.60-0.80	%
	Shrinkage rate	MD	ISO 2577	0.60-0.80	%
		Shrinkage rate	TD:2.00mm3	ISO 294-4	0.75	%
		Shrinkage rate	Shrinkage rate	MD:2.00mm3	ISO 294-4	0.70	%
Water absorption rate	Saturation,23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 4
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 2
Dissipation factor	23°C,1MHz	IEC 60250	9E-03
Dissipation factor	Dissipation factor	23°C,100Hz	IEC 60250	5E-04
Relative permittivity	23°C,1MHz	IEC 60250	3.00
Relative permittivity	Relative permittivity	23°C,100Hz	IEC 60250	3.10
Dielectric strength	23°C,1.00mm	IEC 60243-1	34	KV/mm
Volume resistivity	23°C	IEC 60093	1E+16	ohms·cm
Surface resistivity		IEC 60093	1E+16	ohms
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test		ISO 2039-1	115	Mpa
film	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water vapor permeability	23°C,85%RH,100μm	ISO 15106-1	15	g/m²/24hr
GasPermeation	CarbonDioxide:23°C,25.4μm	ISO 2556	16900	cm³/m²/bar/24hr
	GasPermeation	CarbonDioxide:23°C,100.0μm	ISO 2556	3800	cm³/m²/bar/24hr
		GasPermeation	Nitrogen:23°C,25.4μm	ISO 2556	510	cm³/m²/bar/24hr
			GasPermeation	Nitrogen:23°C,100.0μm	ISO 2556	120	cm³/m²/bar/24hr
				GasPermeation	Oxygen:23°C,25.4μm	ISO 2556	2760	cm³/m²/bar/24hr
				GasPermeation	GasPermeation	Oxygen:23°C,100.0μm	ISO 2556	670	cm³/m²/bar/24hr
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Electrolytic corrosion	23°C	IEC 60426	A1

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.