optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Refractive index		ASTM D542	1.586
Refractive index	Refractive index		ISO 489	1.586
transmissivity		ASTM D1003	86.0to90.0	%
turbidity		ASTM D1003	1.0	%
impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of cantilever beam gap	-30°C	ASTM D256	590	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	910	J/m
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	71	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	81	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile strain	Yield	ISO 527-2/50	6.0	%
elongation	Break	ASTM D638	170	%
Tensile strain	Break	ISO 527-2/50	170	%
Bending modulus		ASTM D790	2340	Mpa
Bending modulus	Bending modulus		ISO 178	2350	Mpa
bending strength		ASTM D790	93.8	Mpa
bending strength	bending strength		ISO 178	94.0	Mpa
Taber wear resistance		ASTM D1044	5	%
Tensile modulus		ASTM D638	2410	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/50	2400	Mpa
tensile strength	Yield	ASTM D638	60.7	Mpa
	tensile strength	Yield	ISO 527-2/50	61.0	Mpa
		tensile strength	Break	ASTM D638	71.7	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	72.0	Mpa
elongation	Yield	ASTM D638	6.0	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Glass transition temperature		ISO 11357-2	150	°C
Glass transition temperature	Glass transition temperature		ASTM D3418	150	°C
Vicat softening temperature	--	ASTM D15256	148	°C
	Vicat softening temperature	--	ASTM D15257	154	°C
		Vicat softening temperature	--	ISO 306/A120	154	°C
		Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	148	°C
Linear coefficient of thermal expansion	MD：-40to82°C	ASTM D696	6.8E-05	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ASTM D792	1.20	g/cm³
density	density		ISO 1183/B	1.20	g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	5.0	g/10min
melt mass-flow rate	melt mass-flow rate	300°C/1.2kg	ISO 1133	5.0	g/10min
Shrinkage rate	MD	ASTM D955	0.50-0.70	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.50-0.70	%
Water absorption rate	23°C,24hr	ASTM D570	0.15	%
	Water absorption rate	23°C,24hr	ISO 62	0.15	%
		Water absorption rate	Equilibrium,23°C,50%RH	ASTM D570	0.32	%
		Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.32	%