| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.13 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 8.00 cm3/10min |
| Shrinkage rate | MD1 | 内部方法 | 0.20-0.60 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.31 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 115 Mpa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.50mm | UL 94 | V-0 |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 36 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.0 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 100 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 8.0 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2/1 | 3900 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 70.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 65.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.0 % |
| Tensile strain | 断裂 | ISO 527-2/5 | 4.0 % |
| Flexural modulus | | ISO 178 | 4000 Mpa |
| bending strength | | ISO 178 | 120 Mpa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| Dissipation Factor | 60Hz | IEC 60250 | 1E-03 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010 |
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 16 KV/mm |
| relative permittivity | 50Hz | IEC 60250 | 2.90 |
| relative permittivity | 60Hz | IEC 60250 | 2.90 |
| relative permittivity | 1MHz | IEC 60250 | 2.80 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| thermal conductivity | | ISO 8302 | 0.21 W/m/K |
| 0.45MPa, Unanealed, 100mm span | | ISO 75-2/Be | 142 °C |
| 1.8MPa, Unanealed, 100mm span | | ISO 75-2/Ae | 137 °C |