PPS Generic PPS - Carbon Fiber Generic

ویژگی‌ها:

Filler carbon fiber reinforced material

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

ویژگی‌ها:

Filler | carbon fiber reinforced material

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of simply supported beam without notch	23°C	ISO 179	15to25	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	3.2to6.0	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180	15to31	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D256	150to500	J/m
Impact strength of cantilever beam gap	23°C	ISO 180	4.9to8.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	42to55	J/m
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Friction coefficient		ASTM D1894	0.14to0.47
bending strength	Yield,23°C	ASTM D790	110to296	MPa
	bending strength	23°C	ISO 178	150to284	MPa
	bending strength	bending strength	23°C	ASTM D790	162to291	MPa
Bending modulus	23°C	ISO 178	12900to24700	MPa
Bending modulus	Bending modulus	23°C	ASTM D790	8790to31500	MPa
elongation	Break,23°C	ISO 527-2	0.68to1.5	%
Tensile modulus	23°C	ASTM D638	9620to35200	MPa
Tensile modulus	Tensile modulus	23°C	ISO 527-2	11100to45000	MPa
tensile strength	Yield,23°C	ASTM D638	57.0to102	MPa
elongation	Yield,23°C	ASTM D638	0.50to1.5	%
elongation	elongation	Break,23°C	ASTM D638	0.50to1.7	%
tensile strength	Break,23°C	ASTM D638	157to160	MPa
	tensile strength	Break,23°C	ISO 527-2	169to176	MPa
	tensile strength	tensile strength	23°C	ASTM D638	89.6to207	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	8.6E-6到2.3E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：--	ASTM D696	3.6E-6到2.1E-5	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	259to270	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	259to272	°C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	275to280	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	260	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	23°C	ISO 294-4	0.12to0.41	%
	Shrinkage rate	TD:23°C	ASTM D955	0.29to0.92	%
	Shrinkage rate	Shrinkage rate	MD:23°C	ASTM D955	0.040to0.20	%
density	23°C	ISO 1183	1.40to1.54	g/cm³
density	density	--	ASTM D792	1.36to1.57	g/cm³
Water absorption rate	23°C,24hr	ASTM D570	0.015to0.020	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity	23°C	ASTM D257	1.0到1.4E+6	ohms·cm
Surface resistivity		ASTM D257	2.0到2.5E+7	ohms
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	23°C	ASTM D785	100to124

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.