physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 11 g/10 min |
Shrinkage rate | 3.20 mm,Flow | ASTM D955 | 0.50 - 0.80 % |
Outdoor applicability | | UL 746C | f1 |
hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Rockwell hardness | R 级 | ASTM D785 | 118 |
optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
transmissivity | 1000 µm | JIS K7361 | 80.0 % |
flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
UL flame retardant rating | 0.50 mm | UL 94 | V-2 |
UL flame retardant rating | 1.6 mm | UL 94 | V-2 |
UL flame retardant rating | 2.5 mm | UL 94 | V-2 |
UL flame retardant rating | 3.0 mm | UL 94 | V-2 |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
tensile strength | 屈服, 3.20 mm | ASTM D638 | 61.8 Mpa |
elongation | 断裂, 3.20 mm | ASTM D638 | > 100 % |
Flexural modulus | 6.40 mm | ASTM D790 | 2260 Mpa |
bending strength | 6.40 mm | ASTM D790 | 93.2 Mpa |
squeeze out | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
drying temperature | | | 100 to 120 °C |
drying time | | | 3.0 to 4.0 hr |
Suggested maximum moisture content | | | 0.020 % |
Temperature in Zone 1 of the material cylinder | | | 260 to 280 °C |
Temperature in Zone 2 of the material cylinder | | | 270 to 300 °C |
Temperature in Zone 3 of the material cylinder | | | 270 to 300 °C |
Temperature in Zone 4 of the material cylinder | | | 270 to 300 °C |
Joint temperature | | | 280 to 300 °C |
Melt Temperature | | | 300 to 320 °C |
die temperature | | | 260 to 295 °C |
injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
drying temperature | | | 100 to 120 °C |
drying time | | | 3.0 to 4.0 hr |
Suggested maximum moisture content | | | 0.020 % |
Temperature at the rear of the barrel | | | 260 to 280 °C |
Temperature in the middle of the barrel | | | 280 to 300 °C |
Temperature at the front of the material cylinder | | | 290 to 310 °C |
Spray nozzle temperature | | | 290 to 310 °C |
Processing (melt) temperature | | | 300 to 320 °C |
Temperature | | | 80 to 120 °C |
Back pressure | | | 0.981 to 3.92 Mpa |
screw speed | | | 40 to 70 rpm |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm,HDT | ASTM D648 | 130 °C |
RTI Elec | | UL 746 | 120 °C |
RTI Imp | | UL 746 | 105 °C |
RTI | | UL 746 | 120 °C |