PC Niblend F17 Soredi S.p.a.

ویژگی‌ها:
Filler glass fiber reinforced material 17% filler by weight
مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	-20°C,3.20mm	ASTM D256	50 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	70 J/m

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	650 °C

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Break	ASTM D638	70.0 MPa
elongation	Break	ASTM D638	3.0 %
Bending modulus		ASTM D790	5000 MPa
bending strength	Break	ASTM D790	100 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	115 °C
Vicat softening temperature		ASTM D15254	123 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	4E-06 cm/cm/°C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20 %
density		ASTM D792	1.23 g/cm³
melt mass-flow rate	260°C/5.0kg	ASTM D1238	18 g/10min
Shrinkage rate	MD	ASTM D955	0.40to0.80 %

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Relative permittivity	1MHz	IEC 60250	2.90
Dissipation factor	1MHz	IEC 60250	0.050
Surface resistivity		IEC 60093	1E+15 ohms
Volume resistivity		IEC 60093	1E+15 ohms·cm
Dielectric strength	1.00mm	IEC 60243-1	25 kV/mm

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	R-Scale	ASTM D785	118