mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ISO 527-1	6100	Mpa
Tensile stress	Break	ISO 527-1	58	Mpa
Elongation at Break		ISO 527-1	4	%
Bending modulus		ISO 178	5400	Mpa
bending strength		ISO 178	100	Mpa
Impact strength of cantilever beam gap	没Notched	ISO 179	60	KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	带Notched	ISO 179	4	KJ/m
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	1.80MPa	ISO 75-1	92	°C
Hot deformation temperature	Hot deformation temperature	0.45Mpa	ISO 75-2	104	°C
Vicat softening temperature		ISO 306	106	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	0.3
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	0.65
UL flame retardant rating		UL 94	V-0
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	Across Flow		0.3-0.5	%
Shrinkage rate	Shrinkage rate	Flow		0.2-0.4	%