برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | after96himmersioninwater:23°C | mg | 83.0 -- |
| Water absorption rate | 饱和,23°C | % | 6.3 -- |
| Water absorption rate | 平衡,23°C,50%RH | % | 1.8 -- |
| Water absorption rate | after24himmersioninwater:23°C | mg | 44.0 -- |
| density | | g/cm³ | 1.14 -- |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M计秤 | | 83 -- |
| Shore hardness | 邵氏D | | 80 -- |
| ball-indentation hardness | | MPa | 145 -- |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 3.00mm | | HB -- |
| UL flame retardant rating | 6.00mm | | HB -- |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| compression stress | 1%应变 | MPa | 22.0 -- |
| Tensile modulus | 23°C | MPa | 3100 1500 |
| tensile strength | 屈服,23°C | MPa | 70.0 45.0 |
| Tensile strain | 断裂,23°C | % | 25 >50 |
| Tensile creep modulus | 1000hr | MPa | 19.0 9.00 |
| compression stress | 5%应变 | MPa | 81.0 -- |
| compression stress | 2%应变 | MPa | 45.0 -- |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 4.0 -- |
| Impact strength of simply supported beam without notch | | | 无断裂 -- |
| Impact strength of cantilever beam gap | | kJ/m² | 4.0 7.0 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dissipation Factor | 100Hz | | 0.015 0.15 |
| Dissipation Factor | 1MHz | | 0.016 0.050 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Surface Resistivity | | ohms | >1.0E+13 >1.0E+12 |
| Volume resistivity | | ohms·cm | >1.0E+14 >1.0E+12 |
| dielectric strength | | kV/mm | 22 14 |
| relative permittivity | 100Hz | | 3.50 6.50 |
| relative permittivity | 1MHz | | 3.10 3.60 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 75.0 -- |
| melting temperature | | °C | 220 -- |
| Linear coefficient of thermal expansion | MD：23到60°C | cm/cm/°C | 8E-05 -- |
| Linear coefficient of thermal expansion | MD：23到100°C | cm/cm/°C | 9E-05 -- |
| thermal conductivity | | W/m/K | 0.29 -- |
| Minimum operating temperature | | °C | -20 -- |
| maximum service temperature | inaircontinuosly | °C | 105 -- |
| maximum service temperature | inairforshortperiods | °C | 170 -- |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.