| other | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| notes | | | 加工温度：180－220℃ |
| characteristic | | | 机械物性；电器特性；挤压加工性 |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | | ASTM D-1238 | 20 g/10min |
| density | | ASTM D-1505 | 0.924 g/cc |
| Shrinkage rate | | | 1-3 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | | ASTM D-1709 | 150 g |
| Shore hardness | | ASTM D-1706 | 53 Shore D |
| Elongation (break point), longitudinal/transverse | | ASTM D-882 | 650/750 % |
| Tensile strength (breaking point) | | ASTM D-638 | 112 |
| Tensile strength (yield point) | | ASTM D-638 | 110 |
| elongation | 断裂 | ASTM D-638 | 650 % |
| tensile strength | | ASTM D-1004 | 115 kg/cm |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| gloss | 45° | ASTM D-2457 | 80 % |
| turbidity | | ASTM D-1009 | 10 % |
| Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792/ISO 1183 | 0.924 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | | ASTM D-1525 | 95 °C |
| melting temperature | | ASTM D-3417 | 124 °C |
| Low temperature brittleness temperature | | ASTM D-746 | <-76 °C |
| vicat | | ASTM D1525/ISO R306 | 95 ℃（℉） |