برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183	1.16 g/cm³
Shrinkage rate	TD:23°C,2.00mm	ISO 294-4	1.4 %
Shrinkage rate	Shrinkage rate	MD:23°C,2.00mm	ISO 294-4	1.2 %
Water absorption rate	23°C,24hr	ISO 62	0.80 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	2.3 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	3.0mm	UL 94	V-0
Burning wire flammability index	0.40mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	0.75mm	IEC 60695-2-12	960 °C
		Burning wire flammability index	1.5mm	IEC 60695-2-12	960 °C
		Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	0.40mm	IEC 60695-2-13	875 °C
	Hot filament ignition temperature	0.75mm	IEC 60695-2-13	875 °C
		Hot filament ignition temperature	1.5mm	IEC 60695-2-13	775 °C
		Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	725 °C
Limiting Oxygen Index		ISO 4589-2	29 %
UL flame retardant rating	0.40mm	UL 94	V-0
	UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-0

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
bending strength	23°C	ISO 178	92.0 MPa
Poisson's ratio		ISO 527-2	0.40
tensile strength	屈服,23°C	ISO 527-2	75.0 MPa
Tensile strain	屈服,23°C	ISO 527-2	5.5 %
Tensile modulus	23°C	ISO 527-2	5000 MPa
Tensile strain	断裂,23°C	ISO 527-2	25 %
Flexural modulus	23°C	ISO 178	3200 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.4 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.4 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	23°C	ISO 180	6.0 kJ/m²

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity	0.750mm	IEC 60093	1E+11 ohms·cm
dielectric strength	1.00mm	IEC 60243	13 kV/mm
arc resistance	3.00mm	ASTM D495	PLC 5
Compared to the Leakage Tracking Index (CTI)	3.00mm	IEC 60112	PLC 0
High arc combustion index (HAI)	0.40mm	UL 746	PLC 0
	High arc combustion index (HAI)	0.75mm	UL 746	PLC 0
		High arc combustion index (HAI)	1.5mm	UL 746	PLC 0
		High arc combustion index (HAI)	High arc combustion index (HAI)	3.0mm	UL 746	PLC 0
High Voltage Arc Traceability Rate (HVTR)	HVTR	UL 746	PLC 1
Hot wire ignition (HWI)	0.40mm	UL 746	PLC 4
	Hot wire ignition (HWI)	0.75mm	UL 746	PLC 4
		Hot wire ignition (HWI)	1.5mm	UL 746	PLC 4
		Hot wire ignition (HWI)	Hot wire ignition (HWI)	3.0mm	UL 746	PLC 3

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
RTI Str	0.40mm	UL 746	100 °C
	RTI Str	0.75mm	UL 746	100 °C
		RTI Str	1.5mm	UL 746	100 °C
		RTI Str	RTI Str	3.0mm	UL 746	110 °C
Hot deformation temperature (HDT)	0.45MPa,未退火，HDT	ISO 75-2/B	225 °C
Hot deformation temperature (HDT)	Hot deformation temperature (HDT)	1.8MPa,未退火，HDT	ISO 75-2/A	65.0 °C
melting temperature		ISO 11357-3	244 °C
线性热膨胀系数	MD：23to55°C,2.00mm	ISO 11359-2	1.1E-04 cm/cm/°C
线性热膨胀系数	线性热膨胀系数	TD：23to55°C,2.00mm	ISO 11359-2	1.1E-04 cm/cm/°C
RTI Elec	0.40mm	UL 746	130 °C
	RTI Elec	0.75mm	UL 746	130 °C
		RTI Elec	1.5mm	UL 746	130 °C
		RTI Elec	RTI Elec	3.0mm	UL 746	130 °C
RTI Imp	0.40mm	UL 746	65.0 °C
	RTI Imp	0.75mm	UL 746	65.0 °C
		RTI Imp	1.5mm	UL 746	85.0 °C
		RTI Imp	RTI Imp	3.0mm	UL 746	85.0 °C