| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 9.0 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.20to0.50 % |
| Water absorption rate | 24hr | ASTM D570 | 0.060 % |
| density | | ASTM D792 | 1.20 g/cm³ |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | L计秤 | ASTM D785 | 106 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Limiting Oxygen Index | | ASTM D2863 | 26 % |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ASTM D638 | 6200 MPa |
| tensile strength | Break | ASTM D638 | 90.3 MPa |
| elongation | Break | ASTM D638 | 2.6 % |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 5800 MPa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 160 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 96 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 120 J/m |
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 650 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 22.6 J |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric strength | 3.20mm,inOil | ASTM D149 | 17 kV/mm |
| dielectric constant | 50Hz | ASTM D150 | 2.86 |
| dielectric constant | 60Hz | ASTM D150 | 2.86 |
| Dissipation Factor | 50Hz | ASTM D150 | 8E-04 |
| Dissipation Factor | 60Hz | ASTM D150 | 8E-04 |
| arc resistance | | ASTM D495 | PLC7 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 4 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| RTI Elec | | UL 746 | 90.0 °C |
| RTI Imp | | UL 746 | 90.0 °C |
| RTI | | UL 746 | 90.0 °C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 141 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 143 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 135 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 138 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 2.9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 8.3E-05 cm/cm/°C |