PUR-Ether//TDI 442 USA Anderson Development
0
مقایسهبرگه داده فنی
| thermosetting | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| STORAGE STABILITY | 2.0 min | ||
| stripping time | 100°C | 15 min | |
| Post curing time | 100°C | 16 hr | |
| 100°C | 16 hr | ||
| STORAGE STABILITY | 4.0to6.0 min | ||
| stripping time | 30 min | ||
| Post curing time | 96°C | 16 hr | |
| STORAGE STABILITY | 2.8 min | ||
| stripping time | 100°C | 15 min | |
| Post curing time | 100°C | 16 hr | |
| STORAGE STABILITY | 2.5to3.0 min | ||
| stripping time | 100°C | 10 min | |
| Post curing time | 100°C | 16 hr | |
| STORAGE STABILITY | 3.0 min | ||
| stripping time | 100°C | 20 min | |
| Post curing time | 100°C | 16 hr | |
| STORAGE STABILITY | 8.0to11 min | ||
| stripping time | 30 min | ||
| Post curing time | 96°C | 16 hr | |
| STORAGE STABILITY | 7.0to9.0 min | ||
| stripping time | 100°C | 25 min | |
| Post curing time | 100°C | 4.0 hr | |
| STORAGE STABILITY | 7.0to8.0 min | ||
| stripping time | 100°C | 25 min | |
| Post curing time | 100°C | 4.0 hr | |
| STORAGE STABILITY | 2.0to3.0 min | ||
| stripping time | 100°C | 20 min | |
| 100°C | 40 min | ||
| Post curing time | 96°C | 16 hr | |
| STORAGE STABILITY | 2.8 min | ||
| stripping time | 100°C | 15 min | |
| Post curing time | 100°C | 16 hr | |
| STORAGE STABILITY | 10to12 min |
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D1505 | 1.07 g/cm³ | |
| Shrinkage rate | MD | ASTM D955 | 1.3 % |
| density | ASTM D1505 | 1.19 g/cm³ | |
| ASTM D1505 | 1.16 g/cm³ | ||
| Shrinkage rate | MD | ASTM D955 | 1.1 % |
| density | ASTM D1505 | 1.13 g/cm³ | |
| ASTM D1505 | 1.20 g/cm³ | ||
| ASTM D1505 | 1.16 g/cm³ | ||
| ASTM D1505 | 1.12 g/cm³ | ||
| Shrinkage rate | MD | ASTM D955 | 1.3 % |
| density | ASTM D1505 | 1.11 g/cm³ | |
| Shrinkage rate | MD | ASTM D955 | 1.5 % |
| density | ASTM D1505 | 1.17 g/cm³ | |
| Shrinkage rate | MD | ASTM D955 | 1.2 % |
| density | ASTM D1505 | 1.14 g/cm³ | |
| ASTM D1505 | 1.12 g/cm³ |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | Shore A | ASTM D2240 | 84 |
| 邵氏D | ASTM D2240 | 76 | |
| 邵氏D | ASTM D2240 | 70 | |
| Shore A | ASTM D2240 | 95 | |
| 邵氏D | ASTM D2240 | 65 | |
| 邵氏D | ASTM D2240 | 75 | |
| 邵氏D | ASTM D2240 | 66 | |
| Shore A | ASTM D2240 | 83 | |
| Shore A | ASTM D2240 | 86 | |
| 邵氏D | ASTM D2240 | 61 | |
| Shore A | ASTM D2240 | 80 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| compressive strength | 5%应变 | ASTM D695 | 0.421 MPa |
| 10%应变 | ASTM D695 | 1.10 MPa | |
| 15%应变 | ASTM D695 | 1.94 MPa | |
| 25%应变 | ASTM D695 | 3.17 MPa |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | Yield | ASTM D412 | 49.6 MPa |
| elongation | Break | ASTM D412 | 250 % |
| compression set | ASTM D395B | 30 % | |
| Shore hardness | ASTM D2632 | 55 % | |
| tensile strength | 100%应变 | ASTM D412 | 39.3 MPa |
| 100%应变 | ASTM D412 | 26.5 MPa | |
| Yield | ASTM D412 | 50.3 MPa | |
| elongation | Break | ASTM D412 | 260 % |
| Break | ASTM D412 | 400 % | |
| compression set | ASTM D395B | 30 % | |
| Shore hardness | ASTM D2632 | 44 % | |
| elongation | Break | ASTM D412 | 310 % |
| compression set | ASTM D395B | 21 % | |
| Shore hardness | ASTM D2632 | 50 % | |
| tensile strength | 100%应变 | ASTM D412 | 13.8 MPa |
| 300%应变 | ASTM D412 | 29.3 MPa | |
| Yield | ASTM D412 | 51.0 MPa | |
| 100%应变 | ASTM D412 | 24.8 MPa | |
| 100%应变 | ASTM D412 | 38.6 MPa | |
| Yield | ASTM D412 | 51.0 MPa | |
| elongation | Break | ASTM D412 | 260 % |
| Shore hardness | ASTM D2632 | 58 % | |
| tensile strength | 100%应变 | ASTM D412 | 25.5 MPa |
| Yield | ASTM D412 | 34.5 MPa | |
| elongation | Break | ASTM D412 | 280 % |
| Shore hardness | ASTM D2632 | 60 % | |
| ASTM D2632 | 56 % | ||
| tensile strength | 100%应变 | ASTM D412 | 3.76 MPa |
| 300%应变 | ASTM D412 | 9.65 MPa | |
| Yield | ASTM D412 | 17.2 MPa | |
| elongation | Break | ASTM D412 | 400 % |
| compression set | ASTM D395B | 29 % | |
| Shore hardness | ASTM D2632 | 30 % | |
| tensile strength | 300%应变 | ASTM D412 | 31.7 MPa |
| Yield | ASTM D412 | 44.1 MPa | |
| elongation | Break | ASTM D412 | 240 % |
| compression set | ASTM D395B | 42 % | |
| Shore hardness | ASTM D2632 | 48 % | |
| tensile strength | 100%应变 | ASTM D412 | 4.48 MPa |
| 100%应变 | ASTM D412 | 6.21 MPa | |
| 300%应变 | ASTM D412 | 15.2 MPa | |
| Yield | ASTM D412 | 23.4 MPa | |
| elongation | Break | ASTM D412 | 400 % |
| compression set | ASTM D395B | 30 % | |
| Shore hardness | ASTM D2632 | 30 % | |
| compression set | ASTM D395B | 36 % | |
| Shore hardness | ASTM D2632 | 58 % | |
| tensile strength | 100%应变 | ASTM D412 | 21.1 MPa |
| 300%应变 | ASTM D412 | 46.7 MPa | |
| Yield | ASTM D412 | 51.0 MPa | |
| 300%应变 | ASTM D412 | 7.96 MPa | |
| Yield | ASTM D412 | 14.8 MPa | |
| elongation | Break | ASTM D412 | 420 % |
| compression set | ASTM D395B | 34 % | |
| Shore hardness | ASTM D2632 | 20 % | |
| tensile strength | 100%应变 | ASTM D412 | 4.69 MPa |
| 300%应变 | ASTM D412 | 8.27 MPa | |
| Yield | ASTM D412 | 31.7 MPa | |
| elongation | Break | ASTM D412 | 550 % |