EHMWPE Quadrant EPP CESTILENE HD 1000 R Mitsubishi Chemical Advanced Materials
0
- ویژگی‌ها:Supplementary information
- کاربردها:Industrial applications
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| Relative Weight Loss | --6 | 内部方法 | 150 |
| thermal conductivity | 23°C | 0.40 W/m/K | |
| Minimum operating temperature | -150 °C | ||
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | <20 % | |
| Relative Weight Loss | --5 | 内部方法 | 180 |
| density | ISO 1183 | 0.930 g/cm³ | |
| Water absorption rate | 饱和,23°C,1.00mm | ISO 62 | 0.020 % |
| molecular weight distribution | 4000000 g/mol | ||
| Shore hardness | 邵氏D,3秒 | ISO 868 | 63 |
| Charpy Notched Impact Strength | --2 | 内部方法 | >80 kJ/m² |
| Partial Break | ISO 179/1eA | >90 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 42.0 °C |
| Shore hardness | 邵氏D,15秒 | ISO 868 | 61 |
| ball-indentation hardness | ISO 2039-1 | 38.0 MPa | |
| Continuous use temperature | --3 | 80.0 °C | |
| --4 | 120 °C | ||
| vicat | ISO 306/B | 80.0 °C | |
| melting temperature | ISO 11357-3 | 130to135 °C | |
| Linear coefficient of thermal expansion | MD：23到100°C | 2E-04 cm/cm/°C | |
| compression stress | 1%应变 | ISO 604/1 | 6.00 MPa |
| 2%应变 | ISO 604/1 | 10.5 MPa | |
| 5%应变 | ISO 604/1 | 18.0 MPa | |
| Tensile modulus | ISO 527-2/1B/1 | 950 MPa | |
| tensile strength | Yield | ISO 527-2/1B/50 | 22.0 MPa |
| Tensile strain | Yield | ISO 527-2/1B/50 | 13 % |
| Nominal tensile fracture strain | ISO 527-2/1B/50 | >50 % |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.