| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.05 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 2.6 g/10min |
| melt mass-flow rate | 230°C/21.6kg | ASTM D1238 | 0.90 g/10min |
| Shrinkage rate | MD：23°C,3.18mm,InjectionMolded | ASTM D955 | 1.9 % |
| Shrinkage rate | TD：23°C,3.18mm,InjectionMolded | ASTM D955 | 1.7 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | ShoreA,1sec,23°C,3.18mm,InjectionMolded | ASTM D2240 | 90 |
| Shore hardness | ShoreA,10sec,23°C,3.18mm,InjectionMolded | ASTM D2240 | 88 |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| OvermoldBonding | | | ABS.PC.ABS/PC.PPO |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Taber abraser | 23°C,1000Cycles,1000g,H-22转轮 | ASTM D3389 | 0.248 mg |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| GardnerImpact | -30°C,3.18mm,InjectionMolded | ASTM D5420 | 14.3 J |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Stretch permanent deformation | 100%应变 | ASTM D412 | 14 % |
| tensile strength | 50%应变 | ASTM D412 | 7.08 MPa |
| tensile strength | 100%应变 | ASTM D412 | 8.03 MPa |
| tear strength | 23°C,3.18mm | ASTM D624 | 53.4 kN/m |
| compression set | 23°C,22hr4 | ASTM D395 | 47 % |
| compression set | 70°C,22hr | ASTM D395 | 94 % |
| compression set | 100°C,22hr | ASTM D395 | 96 % |
| tensile strength | 300%应变 | ASTM D412 | 10.3 MPa |
| tensile strength | Yield | ASTM D412 | 10.4 MPa |
| elongation | Break | ASTM D412 | 330 % |