PA+PP SCHULABLEND® (PA/PP) M/MO GF 25 A SCHULMAN USA
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 108 MPa |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 184 °C |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| density | ISO 1183/A | 1.20 g/cm³ | |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 4.00 cm³/10min |
| Tensile modulus | ISO 527-2/1A/1 | 6700 MPa | |
| tensile strength | Break | ISO 527-2/1A/5 | 103 MPa |
| Tensile strain | Break | ISO 527-2/1A/5 | 3.0 % |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 6.0 kJ/m² |
| 23°C | ISO 179/1eA | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 55 kJ/m² |
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| UL flame retardant rating | 1.6mm | IEC 60695-11-10,-20 | HB |