برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 2.00to2.20 g/cm³ |
| Apparent density | | ISO 60 | 0.90to1.10 g/cm³ |
| Shrinkage rate | MD2 | ISO 2577 | 0.30to0.60 % |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.60 % |
| Shrinkage rate | | ISO 2577 | <0.10 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compression molding pressure | | | >10.0 MPa |
| Compression molding temperature | | | 165to180 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flexural modulus | Compression Molded | ISO 178 | 16000to20000 MPa |
| bending strength | Compression Molded | ISO 178 | 60.0to80.0 MPa |
| compression stress | | ISO 604 | 150to200 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO 179/1eA | 2.0to2.5 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO 179/1eU | 3.0to4.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+12到1.0E+13 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+13到1.0E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 25to35 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| relative permittivity | 100Hz | IEC 60250 | 5.006.00 |
| relative permittivity | 1MHz | IEC 60250 | 4.005.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010to0.030 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010to0.030 |
| arc resistance | | ASTM D495 | PLC 4 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：50到100°C | ISO 11359-2 | 1.0E-5到2.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.90to1.1 W/m/K |
| maximum service temperature | <50h | IEC 60216 | 200 °C |
| maximum service temperature | 20,000h | IEC 60216 | 160 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | >200 °C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 150to170 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.