برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.27 g/cm³ |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 18 g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.25 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 1.3 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M级 | ASTM D785 | 109 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| UL flame retardant rating | 3.0mm | UL 94 | 5VA |
| Limiting Oxygen Index | | ASTM D2863 | 44 % |
| NBSSmokeDensity-Flaming,Ds,4min | | ASTME662 | 2.00 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ASTM D638 | 3590 Mpa |
| tensile strength | 屈服 | ASTM D638 | 110 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| elongation | 断裂 | ASTM D638 | 60 % |
| Flexural modulus | 100mmSpan | ASTM D790 | 3520 Mpa |
| bending strength | Yield,100mmSpan | ASTM D790 | 165 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 1200 J/m |
| Dart impact | 23°C | ASTM D3029 | 33.9 J |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 1E+17 ohms·cm |
| dielectric strength | 1.60mm,inAir | ASTM D149 | 33 KV/mm |
| dielectric strength | 1.60mm,在油中 | ASTM D149 | 28 KV/mm |
| dielectric constant | 1kHz | ASTM D150 | 3.15 |
| Dissipation Factor | 1kHz | ASTM D150 | 1.3E-03 |
| Dissipation Factor | 2.45GHz | ASTM D150 | 2.5E-03 |
| arc resistance | | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 5.6E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.22 W/m/K |
| RTI Elec | | UL 746 | 170 °C |
| RTI Imp | | UL 746 | 170 °C |
| RTI Str | | UL 746 | 170 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 207 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 199 °C |
| vicat | | ASTM D15255 | 219 °C |