PA TROGAMID® CX CX9704 Altuglas International of Arkema Inc.

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	0°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	-30°C,Complete Break	ISO 179/1eA	10	kJ/m²
	Charpy Notched Impact Strength	0°C,Complete Break	ISO 179/1eA	11	kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,Complete Break	ISO 179/1eA	11	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.8mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	HB
Burning wire flammability index	1.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	825	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus	23°C	ISO 527-2	1400	MPa
tensile strength	Yield,23°C	ISO 527-2/50	60.0	MPa
Tensile strain	Yield,23°C	ISO 527-2/50	8.0	%
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50	%
Bending modulus		ISO 178	1500	MPa
bending strength	3.5%Strain	ISO 178	50.0	MPa
bending strength	bending strength	--	ISO 178	90.0	MPa
OuterFiberStrain Atmospheric Stress		ISO 178	>10	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	102	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	120	°C
Glass transition temperature		ISO 11357-2	132	°C
Vicat softening temperature	--	ISO 306/A	132	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B	125	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	9E-05	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density	23°C	ISO 1183	1.02	g/cm³
Stickiness		ISO 307	>120	cm³/g
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dissipation factor	23°C,1MHz	IEC 60250	0.022
Compared to the anti leakage trace index	--4	IEC 60112	PLC 1
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Surface resistivity		IEC 60093	1E+14	ohms
Volume resistivity		IEC 60093	1E+15	ohms·cm
Relative permittivity	23°C,100Hz	IEC 60250	3.40
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	3.30
Dissipation factor	23°C,100Hz	IEC 60250	0.013
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shore hardness	ShoreD	ISO 868	81
Ball Pressure Test		ISO 2039-1	110	MPa

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.