برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.31 g/cm³ |
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 19 g/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.6 % |
| Shrinkage rate | MD | ISO 294-4 | 1.7 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.40 % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.20 % |
| viscosity number | | ISO 307 | 130 cm³/g |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.8mm | UL 94,IEC60695-11-10,-20 | HB |
| UL flame retardant rating | 1.5mm | UL 94,IEC60695-11-10,-20 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 22 % |
| FMVSS flammability | | FMVSS302 | SE/NBR |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Nominal tensile fracture strain | | ISO 527-2 | 30 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 2600 Mpa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1800 Mpa |
| bending strength | | ISO 178 | 88.0 Mpa |
| Tensile modulus | | ISO 527-2 | 2600 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 59.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 8.0 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 3.5 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.5 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.0 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 70 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 140 kJ/m² |
| Filling analysis | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt density | | | 1.11 g/cm³ |
| Ejection Temperature | | | 170 °C |
| SpecificHeatCapacity of Melt | | | 2100 J/kg/°C |
| ThermalConductivityofMelt | | | 0.21 W/m/K |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 26 KV/mm |
| relative permittivity | 100Hz | IEC 60250 | 3.80 |
| relative permittivity | 1MHz | IEC 60250 | 3.20 |
| Dissipation Factor | 100Hz | IEC 60250 | 2E-03 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 145 °C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 180 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 60.0 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 60.0 °C |
| vicat | | ISO 306/B50 | 175 °C |
| melting temperature | | ISO 11357-3 | 225 °C |
| Crystallization peak temperature | | ISO 11357-3 | 192 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.3E-04 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.