ASA Generic ASA+PC Generic

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dart impact	23°C	ASTM D3763	35.3to47.9	J
Impact strength of cantilever beam gap	23°C	ISO 180	16to61	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	140to600	J/m
Charpy Notched Impact Strength	23°C	ISO 179	5.0to62	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot filament ignition temperature		IEC 60695-2-13	550to960	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Yield,23°C	ISO 527-2	54.6to62.4	MPa
tensile strength	tensile strength	Yield,23°C	ASTM D638	52.9to65.6	MPa
Tensile modulus	23°C	ISO 527-2	2120to2760	MPa
Tensile modulus	Tensile modulus	23°C	ASTM D638	2540to2720	MPa
tensile strength	Break,23°C	ASTM D638	44.0to66.0	MPa
tensile strength	tensile strength	Break,23°C	ISO 527-2	39.0to64.3	MPa
elongation	Yield,23°C	ASTM D638	3.7to6.1	%
	elongation	Yield,23°C	ISO 527-2	2.3to8.7	%
		elongation	Break,23°C	ASTM D638	23to100	%
		elongation	elongation	Break,23°C	ISO 527-2	36to80	%
Bending modulus	23°C	ASTM D790	2080to2770	MPa
Bending modulus	Bending modulus	23°C	ISO 178	2000to2640	MPa
bending strength	23°C	ASTM D790	68.0to94.0	MPa
	bending strength	23°C	ISO 178	72.8to97.5	MPa
	bending strength	bending strength	Yield,23°C	ASTM D790	81.7to95.4	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	102to130	°C
Linear coefficient of thermal expansion	TD	ISO 11359-2	7.1E-5到7.8E-5	cm/cm/°C
	Linear coefficient of thermal expansion	TD	ASTME831	7.2E-5到7.9E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.0E-5到8.6E-5	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	98.4to132	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	87.7to113	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	87.2to122	°C
Vicat softening temperature	--	ASTM D1525	104to138	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306	102to139	°C
Linear coefficient of thermal expansion	MD	ASTME831	7.2E-5到7.3E-5	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	23°C,24hr	ASTM D570	0.10to0.25	%
Shrinkage rate	23°C	ISO 294-4	0.59to0.70	%
Shrinkage rate	Shrinkage rate	MD:23°C	ASTM D955	0.50to0.60	%
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	17.0to26.0	cm³/10min
melt mass-flow rate	260°C/5.0kg	ISO 1133	19to40	g/10min
melt mass-flow rate	melt mass-flow rate	260°C/5.0kg	ASTM D1238	14to45	g/10min
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20to0.30	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.60to1.0	%
density	--	ASTM D792	1.10to1.25	g/cm³
density	density	23°C	ISO 1183	1.11to1.20	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity	23°C	IEC 60093	1.0E+13到1.0E+15	ohms·cm
Surface resistivity		IEC 60093	1.0E+13到1.0E+15	ohms
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test		ISO 2039-1	88.7to110	MPa
Rockwell hardness	23°C	ASTM D785	109to116